今天给大家分享的是2014年5月份 《Nano Research》上发表的一篇名为：Mesocrystal Co3O4 nanoplaets as high capacity anode materials for Li-ion batteries
文章摘要如下：

Faceted crystals with exposed highly reactive planes have attracted intensive investigations for applications. Herein, we demonstrate a general synthetic method to prepare mesocrystal Co3O4 with predominantly exposed {111} reactive facets by the in situ thermal decomposition from Co(OH)2 nanoplaets. The mesocrystal feature was identified by field emission scanning electron microscopy, transmission electron microscopy, selected area electron diffraction, and N2 isotherm analyses. When applied as anode material in lithium-ion batteries, mesocrystal Co3O4 nanoplaets delivered a high specific capacity and an outstanding high rate performance. The superior electrochemical performance should be ascribed to the predominantly exposed {111} active facets and highly accessible surfaces. This synthetic strategy could be extended to prepare other mesocrystal functional nanomaterials.

该文章中材料表征采用的是美国麦克仪器3Flex

详情可参考下面链接：

http://link.springer.com/article/10.1007/s12274-014-0440-0