基于蓝宝石衬底的全区域覆盖的单层二硫化锡_二维材料薄膜-泰州巨纳新能源有限公司

基于蓝宝石衬底的全区域覆盖的单层二硫化锡返回列表页

参考价: ￥ 6979.7

订货量: ≥1 片

具体成交价以合同协议为准

产品型号

品牌2D Semiconductors

厂商性质生产商

所在地泰州市

在线询价加入对比查看联系电话

更新时间：2024-06-03 19:29:17浏览次数：1033次

联系我时，请告知来自化工仪器网

供货周期	现货	应用领域	环保,化工,能源,综合

This product contains full area coverage SnS2 monolayers on c-cut sapphire substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick SnS2 sheet. Synthesized full area coverage monolayer SnS2 is highly crystalline, some regions also display significant crystalline anisotropy.

Sample Properties.

Sample size	1cm x 1cm square shaped
Substrate type	Sapphire c-cut (0001)
Coverage	Full monolayer coverage
Electrical properties	2.2 eV Indirect Gap Semiconductor
Crystal structure	Hexagonal Phase
Unit cell parameters	a = b = 0.362, c = 0.590 nm, α = β = 90°, γ = 120°
Production method	Low Pressure Chemical Vapor Deposition (LPCVD)
Characterization methods	Raman, angle resolved Raman spectroscopy, photoluminescence, absorption spectroscopy TEM, EDS

Specifications

1) Identification. Full coverage 100% monolayer SnS2 uniformly covered across c-cut sapphire

2) Physical dimensions. One centimeter in size. Larger sizes up to 2-inch wafer-scale available upon requests.

3) Smoothness. Atomically smooth surface with roughness < 0.15 nm.

4) Uniformity. Highly uniform surface morphology. SnS2 monolayers uniformly cover across the sample.

5) Purity. 99.9995% purity as determined by nano-SIMS measurements

6) Reliability. Repeatable Raman and photoluminescence response

7) Crystallinity. High crystalline quality, Raman response, and photoluminescence emission comparable to single crystalline monolayer flakes.

8) Substrate. c-cut Sapphire but our research and development team can transfer SnS2 monolayers onto variety of substrates including PET, quartz, and SiO2/Si without significant compromisation of material quality.

9) Defect profile. SnS2 monolayers do not contain intentional dopants or defects. However, our technical staff can produce defected SnS2 using α-bombardment technique.

Supporting datasets [for 100% Full area SnS2 monolayers on c-cut Sapphire]

Transmission electron images (TEM) acquired from CVD grown full area coverage SnS2 monolayers on c-cut sapphire confirming high crystallinity

Energy dispersive X-ray spectroscopy (EDX) characterization on CVD grown full area coverage monolayer SnS2 on c-cut sapphire

Raman spectroscopy measurement confirm monolayer nature of the CVD grown samples and shows the high crystallinity of the CVD samples. PL spectrum does not show any PL signal due to indirect band nature.