现货 110-19 聚酰亚胺导电胶

现货 110-19  聚酰亚胺导电胶

说明：110-19是一种单组分、银填充、导电聚酰亚胺粘合剂，适用于

通过冲压、丝网印刷、浸渍和注射器分配应用。这个产品是为装配而设计的

电气和电子部件。固化计划允许快速处理和由此产生的粘结展示

优异的热稳定性和高温附着力。

典型固化特性：

稠度光滑膏

填充银

银含量，固化>81

玻璃变压器。临时雇员。（摄氏度）>250

体积电阻率（Ω-cm）0.0001

可焊性编号

水解稳定性优异

有效温度范围（℃）-55至+270

热稳定性（摄氏度）达到325

T-抗剪强度（psi）>1250

热导率（w/mk）8.13

建议的处理和固化：110-19已准备好供应使用。在表面涂上粘合剂

用手工和/或自动方法粘合和装配。施加轻微压力以确保表面良好配合

以及菲力的形成。在170°C至180°C下固化1小时后，大多数应用的性能佳。良好

通过在120°C至150°C的温度下固化，可在多种基底上获得性能。

一般在150℃下固化30分钟。建议终用户通过实验确定温度和时间

适合个人应用。

贮存期：在-5°C下保存1年。

安全和操作：在通风良好的情况下使用。远离火花和明火。避免长时间

接触皮肤和吸入蒸汽。用肥皂和水清洗皮肤。

现货 110-19  聚酰亚胺导电胶

DESCRIPTION: 110-19 is a single component, silver filled, electrically conductive polyimide adhesive suitable for
application by stamping, screen printing, dipping and syringe dispensing. This product is designed for assembling
electrical and electronic components. The cure schedule allows for rapid processing and the resulting bond exhibits
excellent thermal stability and adhesion at high temperatures.
TYPICAL CURED PROPERTIES:

Consistency Smooth Paste
 Filler Silver
 Percent Silver, cured > 81
 Glass Trans. Temp. (°C) > 250
 Volume Resistivity (Ω-cm) 0.0001
 Solderable No
 Hydrolytic Stability Excellent
 Useful Temperature Range (°C) -55 to +270
 Thermal Stability (°C) Good to 325
 T-Shear Strength (psi) >1250
Thermal Conductivity (W/mK) 8.13
SUGGESTED HANDLING & CURING: 110-19 is ready to use as supplied. Apply adhesive to surface to be
bonded by hand and/or automatic method and assemble. Apply slight pressure to assure good mating of surfaces
and formation of filet. Best properties for most applications result when cured for l hour at 170°C to 180°C. Good
properties are obtained on a variety of substrates by curing at temperatures ranging from 120°C to 150°C. Most
popular cure is 30 minutes at 150°C. End user is advised to experimentally determine temperature and time best
suited for individual applications.
STORAGE: Shelf Life: 1 year at -5°C.